Powder coatings are also called 4E products because of their environmental protection, energy saving, safety, and economy.
1. Product type analysis:
| Product name | Type | Product description | Standard | Weathering life |
|---|---|---|---|---|
| PCNH | Super Weathering | Made of special super weathering resin, inorganic ceramic pigment and special additives, used for outdoor high-end weathering products | AAMA2603-02 | >10Y |
| PCNF | modified fluorocarbon | The fluorocarbon powder, which is a combination of fluorine-modified, stable bond-modified super-weather-resistant resin and inorganic special pigments, has the characteristics of super weather resistance, high hardness, water cleaning resistance, acid, alkali and salt resistance. | AAMA2604-05 | >15Y |
| PVDF | fluorocarbon | It is developed with 70% fluorocarbon and special pigment fillers, and has the characteristics of high hardness, easy cleaning, solvent resistance, acid, alkali and salt resistance, anti-aging, high weather resistance, etc., commonly known as the “king of coatings”. | GB/T23443-2009 AAMA2605-05 | >20Y |
| FEVE | thermosetting fluorocarbon | 70% fluorine content, belongs to thermosetting fluorocarbon powder coating, and the production process and cost are relatively high. | AAMA2605-05 | >20Y |
2. Fluorocarbon powder construction process:
1) Pre-treatment requirements:
Aluminum parts need to be chromized or passivated before spraying fluorocarbon powder coatings, so that the product can achieve the best performance after spraying.
2) Spraying parameter range:
The distance between the electrostatic gun and the workpiece is 120-180mm, the voltage is 40-80KV, and the current is 10-20uA. Due to the differences between various electrostatic spray guns, it is recommended that the atomization parameters and powder output be adjusted according to the needs of the site.
3) Product parameters:
Curing temperature: 235±5℃ (actual heating temperature of the workpiece)
Curing time: 15-20min
3. Comparison between fluorocarbon powder and fluorocarbon paint:
| SafetyProject | Liquid fluorocarbon coating | Powder fluorocarbon coating |
|---|---|---|
| Coating equipment | Liquid coating line | Powder coating line |
| Solvent use | 70% solvent | Solvent-free |
| Coating use rate | 35-60% | 95-100% |
| Energy consumption | Very large | Small |
| Environmental protection | A large amount of organic solvents evaporate, which is harmful to the environment | Environmental protection, VOC emissions are infinitely close to 0 |
| Safety | Flammable and explosive, unsafe | Very high safety |
| Cost | High cost | Low cost |
| Coating composition | 70% PVDF content | Same as liquid coating |
| Weather resistance | Meets AAMA2605 standard | Same as liquid coating |
| Hardness | Softer | Very high |
| Abrasion resistance | Good | Very good |
| Usage license | Required | Required |
| Flatness | Very good | Similar to liquid coating |
| Application performance | Liquid fluorocarbon coating Powder | fluorocarbon coating |
|---|---|---|
| Substrate | Aluminum substrate, epoxy primer substrate, zinc-rich substrate | Same as liquid coating |
| Pretreatment | Pre-treat the surface to make it meet AAMA2605 | Same as liquid coating |
| Film thickness | Two coatings: 30~40um; multiple coatings: above 40um | 50~80um |
| Curing treatment | 232~249℃PMT(10~20min) | Same as liquid coating |
| Utilization rate | ~50% | ~100% |
| Environmental protection | A large amount of harmful solvents evaporate, waste liquid and waste residue | No volatile solvents |
| Solvents | A large amount of solvents are required | No solvents |
| Color difference | The color difference is affected by process changes | The color difference is slightly affected by process changes |
| Solid content | about 40% | 100% |
| Gloss (60°) | 15~35° | 15~60° |
| Pencil hardness | ≥F | ≥2H |
| Abrasion resistance | Friction coefficient 555±10 | Slightly higher |
| Solvent resistance | MEK rubs back and forth 100 times | Same as liquid coating |
| Wet/dry paint adhesion | The film does not peel off after removing the tape | Same as liquid coating |
| Salt spray resistance 1000h | The line becomes bare metal 1/32 inch | Same as liquid coating |
| Gloss retention | Accelerated aging test according to AAMA2605 standard, gloss retention 50% | Same as liquid coating |
| Color retention/powdering | According to AAMA2605 standard, color difference ≤5. powdering rate ≥8 | Same as liquid coating |
4. Naming and display of related products:
| Product name | Type | Series naming | Particle size |
|---|---|---|---|
| PCNH | Super weather-resistant | permanent series~No 1 | 34~38um |
| PCNF | Modified fluorocarbon | permanent series~No 2 | 28~36um |
| PVDF | Fluorocarbon | permanent series~No 3 | 28~36um |
| FEVE | Thermosetting fluorocarbon | permanent series~No 4 | 28~36um |
5. Application scope:
Suitable for walls or steel structures with super weather resistance requirements and landmark buildings, widely used in protective coatings such as exhibition centers, government buildings, bridges, etc. Applicable to various outdoor metal products: such as metal curtain wall aluminum profiles, open-air stadium seats, ceiling material coatings, sports equipment outdoor lamps, industrial equipment, auto parts, etc.
6. Testing standards
AAMA2603
| Serial number | Test item | Test method | Required index |
|---|---|---|---|
| 1 | Powder particle size | Particle size analyzer | ≤10um ≤10% DV50 34~38um |
| 2 | Coating appearance/color/color difference | AAMA2603 | Observe surface defects at 3 meters and 900. The color is within the agreed range. |
| 3 | Film thickness | AAMA2603 | 80% of the local film thickness ≥20um; local film thickness ≥17 um |
| 4 | Gloss (60°) | AAMA2603 | ±5 units |
| 5 | Dry film adhesion | AAMA2603 | Cross-cut spacing 1mm, no boiling water adhesion |
| 6 | Pencil hardness | AAMA2603 | ≥1.MinimumH |
| 7 | Impact test | AAMA2603 | 18N·M, (3±0.3)mm, same as standard test panel |
| 8 | Neutral smoke test (NSS) | AAMA2603 | NSS 1000h Minimum rating of seven，Minimum blister of eight |
| 9 | Moisture and heat resistance | AAMA2603 | 380C，100%RH，1500h |
| 10 | Weather resistance | AAMA2603 | Xenon lamp 1000h Florida ≥1 year |
Previous post：Metal Bond Powder Coatings
Next chapter：FEVE fluorocarbon powder coating
PRODUCT
NEWS
- Principle, Usage and Dosage of Fluorescent Whitening Agent 2025-09
- How to make beeswax? 2025-09
- Chinese Rhus Wax Usage and Production Process 2025-08
- Emulsified wax classification and principle 2025-08
- Thermoplastic acrylic resin 2025-08
- LUBRITECH-300: High-Performance Lubricant Overview 2025-04
- BIOPLAST-200: Biodegradable Plastic Overview 2025-04
- POLYFIBER-900: Reinforcement Fiber Overview 2025-04
- CLEANSOL-400: Industrial Cleaner Overview 2025-04
- FLEXIPLAST-600: Flexible Plastic Overview 2025-04
TEL：+86-21-6420 0566 Copyright © 2021-2024 Shanghai Qinsun Co., Ltd. All Rights Reserved. qinsun
Address：No.258 Ban Ting road, Song Jiang district, Shanghai