Use of nitrocellulose varnish in wood additives
Email：services@moutainchem.com
Specifications：
Product details
Nitrocellulose varnish has unique advantages in wood coating. The rational use of additives can further improve its performance. From leveling agents to defoamers, from dispersants to anti-settling agents, various additives help nitrocellulose varnish create a perfect wood coating.
Used as dispersant
Used as defoaming agent
Used as leveling agent
Used as anti-sagging agent
Used as dispersant
| Product | Main | Type | NV | Product features | Application fields |
| Component | (%) | ||||
| CFC-500HP | Polycarboxylic | Primer | 50 | -Superior dispersing and storage stability in | -Short, medium, long oil alkyd |
| acid with | & | co-grinding system for organic and | coatings | ||
| amine salt | Topcoat | inorganic pigments | -Chlorinated rubber, epoxy | ||
| -Improve gloss and anti-flooding | coatings | ||||
| -Promote flow property and hiding power | -Alkyd, acrylic, polyester baking | ||||
| -Improve dispersion and thixotropicproperty | system | ||||
| in co-grinding with bentonite | |||||
| CFC-510 | Polycarboxylic | Primer | 52 | -Superiorwetting,dispersingforTiO2and | -Automotive,refinishcoating |
| acid | & | inorganicpigments | system | ||
| copolymer | Topcoat | -Superiorglossanddeflocoulation | -Generalindustrialbakingsystem | ||
| -Superiordispersingforhighconcentration | -Oilfreepolyestercoatings | ||||
| pigments | -Coilcoatings | ||||
| -ImproveDOIandhidingpower | |||||
| -Improvelevelingandanti-flooding | |||||
| CFC-530 | High | Primer | 98 | -Reduce the viscosity of the carbon black | -Pigment concentrates in polyols, |
| molecular | & | -Superior wetting dispersing for organic and | plasticizers, unsaturated | ||
| copolymer | Topcoat | inorganic pigment | polyesters. | ||
| -Superior storage stability due to it’s | -Automotive Refinish Coating | ||||
| deflocculation | system | ||||
| -Epoxy system |
Used as defoaming agent
| Product | Main | Type | NV | Product features | Application fields |
| Component | (%) | ||||
| Depol | Special high | Primer | 1.5 | -Superior defoaming, deaeratingfor organic | -Wood coatings based on short oil |
| CFC-165 | molecular | & | solvent system | alkyd | |
| compound | Topcoat | -No gloss reduction of surface film | -Acrylic lacquer, acrylic urethane | ||
| -Excellent deaeratingperformance during | coatings | ||||
| spraying, roller and brushing coatings | -Epoxy coating system | ||||
| -Prevent crateringand flooding | -Medium, long oil enamel coatings | ||||
| Depol | Polyvinyl | Primer | 20 | -Hazeoffilmisnothappenedatevenhigh | -Alkyd,lacquer,fastairdrying |
| CFC-192 | ether with | & | dosageofaddition | enamelsystem | |
| modified | Topcoat | -Nocrateringproblemduringdefoaming, | -Polyurethane,epoxycoatings | ||
| acrylic | deaerating | -Chlorinatedrubber,polyesterhigh | |||
| copolymer | -Excellentdeaeratingperformanceduring | temperaturebakingsystem | |||
| spraying,rollerandbrushingcoatings |
Used as leveling agent
| Product | Main | Type | NV | Product features | Application fields |
| Component | (%) | ||||
| Letch | Polyacrylic | Primer | 50 | -Anti-floodinganddefoamingfororganic | -Acrylichightemperaturebaking |
| CFC-54 | ester | & | solventsystem | system | |
| copolymer | Top coat | -Excellentcompatibilitywithorganicsolvent | -Epoxycoatingsforfloor | ||
| system | -Organicsolventcoatingsystem | ||||
| -Improvelevelingandpreventcrateringfor | -Powdercoatings | ||||
| bakingsystem | |||||
| -Goodlevelinginsolventandsolventfree | |||||
| basedepoxycoatingsforfloor | |||||
| Slip | Polyether | Primer | 52 | -Improve slip and surface hardness for drying | -Acrylic air drying and acrylic |
| CFC-700 | modified | & | films | urethane low temperature baking | |
| polysiloxane | Top coat | -Prevent silkingand crateringdue to it`s | system | ||
| copolymer | superior leveling | -Alkyd, acrylic baking system for | |||
| -Excellent workability due to it`s prevent | industrial paints | ||||
| blocking | -Pure epoxy, urethane coatings | ||||
| -Improve gloss of surface films | |||||
| Slip | Polyether | Primer | 12 | -Superior compatibility with overall organic | -Water soluble acrylic air drying |
| CFC-706 | modified | & | solvent system | and baking system | |
| polysiloxane | Top coat | -Prevent blocking for drying films | -Solvent based acrylic urethane | ||
| copolymer | -Improve leveling and slip, anti-cratering | and acrylic air drying system | |||
| -Improve gloss for acrylic and acrylic | -Solvent based acrylic, polyester | ||||
| urethane coatings | high temperature baking system | ||||
| -Polyurethane coatings |
Used as anti-sagging agent
| Product | Main | Type | NV | Product features | Application fields |
| Component | (%) | ||||
| CIMA-222 | Special | Primer | 20 | -Goodthixotropicpropertyinwiderange | -Metallic and mica type of general |
| nitrogen | coatingsystem | industrial coatings | |||
| contained | -Superiorstoragestabilityandnoseeding | -High build type of heavy-duty | |||
| compound | formation | coatings | |||
| -Canbedispersedinwiderangetemperature | -Tar epoxy, tar urethane, pure | ||||
| -Noinfluenceoninter-adhesivepropertyfor | epoxy, chlorinated rubber coatings | ||||
| systemcoatings | -General industrial coating system | ||||
| CIMA | Special | Primer | 20 | -Metallic and mica type of general | |
| 240-20 | nitrogen | industrial coatings | |||
| contained | -High build type of heavy-duty | ||||
| compound | coatings | ||||
| -Tar epoxy, tar urethane, pure | |||||
| epoxy, chlorinated rubber coatings | |||||
| CIMA | Special | Primer | 20 | -Good thixotropicproperty in wide range | -Alkyd, acrylic melamine based |
| 300-20 | nitrogen | & | coating system | general industrial coatings | |
| contained | Top coat | -Can be dispersed in wide range temperature | -Alkyd, polyester modified heat | ||
| compound | -Superior storage stability and no seeding | resistant coatings | |||
| formation | -Chlorinated rubber, wash primer | ||||
| -No influence on inter-adhesive property for | coatings | ||||
| system coatings | -High build type of epoxy based | ||||
| -Anti-settling and improve the orientation of | heavy-duty coatings | ||||
| metallic pigments |
Previous post：Industrial paint for epoxy
Next chapter：Polyester / aminoolacid (heated dry)
PRODUCT
NEWS
- What are some color matching techniques for powder coatings? 2025-11
- Principle, Usage and Dosage of Fluorescent Whitening Agent 2025-09
- How to make beeswax? 2025-09
- Chinese Rhus Wax Usage and Production Process 2025-08
- Emulsified wax classification and principle 2025-08
- Thermoplastic acrylic resin 2025-08
- LUBRITECH-300: High-Performance Lubricant Overview 2025-04
- BIOPLAST-200: Biodegradable Plastic Overview 2025-04
- POLYFIBER-900: Reinforcement Fiber Overview 2025-04
- CLEANSOL-400: Industrial Cleaner Overview 2025-04
TEL：+86-21-6420 0566 Copyright © 2021-2024 Shanghai Qinsun Co., Ltd. All Rights Reserved. qinsun
Address：No.258 Ban Ting road, Song Jiang district, Shanghai